Abstract
The dry tribological behavior of a Ti–50.3 at.% Ni alloy at temperatures of 25 °C, 50 °C and 200 °C was studied. The wear tests were performed on a high temperature pin-on-disk tribometer using 52100 steel and tungsten carbide pins. The worn surfaces of the NiTi alloy were examined by scanning electron microscope. The results showed that in the wear tests involving steel pins, the wear rate of the NiTi decreased as the wear testing temperature was increased. However, for the NiTi/WC contact, a reverse trend was observed. There was also a large decrease in the coefficient of friction for the NiTi/steel contact with increasing wear testing temperature. The formation of compact tribological layers could be the main reason for the reduction of the wear rate and coefficient of friction of the NiTi/steel contact at higher wear testing temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.