Abstract

AbstractElastomeric polymers such as high‐density polyethylene, have a variety of desirable features, that have supplanted traditional materials. However, high‐density polyethylene (HDPE) shows inadequate wear resistance, which limits its use for industrial applications, particularly in low‐load‐bearing applications such as flexible energy harvesting devices and sensors. The current work is engrossed in investigating the influence of hybrid reinforcements CaCO3 particles and bentonite nano clay as secondary reinforcements in high‐density polyethylene (HDPE)‐based composites on the wear and friction properties. The reinforcements were melt compounded with HDPE using a Brabender mixer and sampled using an injection molding machine. The wear test (ASTM G‐99‐04) was performed by a pin‐on‐disk tribo‐tester. In comparison to a base matrix, the synthesized hybrid composite achieved the maximum improvement in wear rate of 93%. The results revealed that there is a significant improvement in wear resistance. Morphological analysis revealed that due to the encapsulation and compatibilization effect of bentonite nano clay the hybrid composite exhibited improved wear performance. The results signify the synergistic effect of filler particles resulted in sufficient bonding for stress transfer due to the encapsulation of CaCO3 by nano clay. The wear mechanism observed optically was abrasion, fatigue, and adhesion wear that changed with the change in the weight percent of nanoparticles. Finally, the prepared composite with enhanced tribological properties such as low wear rate, low friction coefficient, and enhanced morphology can be used in low load‐bearing wear applications such as turbo nanogenerators and piezo nanogenerators.Highlights Bentonite nano clay and CaCO3 dispersed homogeneously in HDPE matrix. Wear resistance of HDPE increases by reinforcing particles (nano‐clay and CaCO3). Micro‐cutting, deformations, and particle husks were the possible wear mechanism. Encapsulation effects the hybrid composite to exhibit improved wear performance.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.