Tribo‐investigation of PEEK‐short carbon fibre composites in severe testing conditions

Abstract

AbstractA series of composites of polyetheretherketone (PEEK) containing short carbon fibre (CF) in the range of 0–30% (w/w) was developed. Their wear behaviour in low amplitude oscillating wear (LAOW) mode was studied under various operating parameters such as load and temperature. The LAOW mode was studied in ball‐on‐plate configuration against steel (100 Cr 6) at ambient temperature and at 100°C. In this mode, the coefficient of friction (µ), specific wear rate (Ko) and limiting loading pressure‐sliding speed (PV) values were investigated. It was observed that with increase in %CF, the wear performance and utility of PEEK (limiting PV value) improved significantly. Thirty percent CF was best performing composite in all aspects. The µ, however, was hardly influenced with the inclusion of CF or variation in operating parameters. The same composites were also evaluated in abrasive wear mode to study the influence of severe operating conditions on wear and friction performance. In this wear mode, the CF‐filled composites showed poorer wear resistance than did neat PEEK. The specific wear rate was correlated with strength properties and it was observed that these composites closely followed the predictions of the Ratner–Lancaster plot. Scanning electron microscopy was used to examine the microstructural features of worn surfaces. Copyright © 2007 John Wiley & Sons, Ltd.