The quaternary Ti-Si-C-N nanocomposite is regarded to be promising one in the biomedical field due to its improved tribocorrosion performance and biocompatibility. The deposition of such material on biomedical components surfaces can extend its lifespan by minimizing wear debris and ion releasing inside the physiological environment. Therefore, this work investigates the tribocorrosion behavior of low friction Ti-Si-C-N nanocomposite coatings applied on the ASTM F136 titanium alloy immersed in a phosphate-buffered solution (PBS). The coatings were obtained by the plasma-enhanced magnetron sputtering (PEMS) technique using an assorted precursor flow range of tetramethylsilane (TMS) and hexamethyldisilazane (HMDSN) liquid along with acetylene (C2H2) gas. Reciprocal sliding tribocorrosion tests were performed under PBS solution on the samples and compared to a Ti-6Al-4V bare alloy sample. The microstructure, morphology, chemical structure, mechanical properties, and adhesion of the coated samples were also evaluated. The results presented an expressive reduction of at least 97% in the wear rate of the low friction Ti-(Si)-C-N nanocomposite coatings compared to the titanium bare alloy sample. The tribocorrosion performance of the coated samples demonstrated a strong correlation within the Silicon and Carbon content presented on coatings chemical compositions. As consequence, the roles of nanocrystallites refinement, the presence of amorphous carbon region and the oxides generation were demonstrated as relevant characteristics to improve the tribocorrosion behavior of Ti-Si-C-N nanocomposite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.