Abstract
In this work, mild steel as a substrate was coated by electrodeposition in a bath mixed with nickel sulfate (NiSO4·6H2O), nickel chloride (NiCl4·6H2O), and boric acid (H3BO3) using nanocomposite cetyltrimethylammonium bromide, hBN, and epoxy with hardener. The experiments were designed using the Taguchi method through the L9 orthogonal array to reduce the number of experiments. The input parameters for the design of experiments were taken: the time (min), voltage (V), and the hBN concentration (wt-%). The coated samples were tested for their tribological, corrosion, and adhesion performance using pin-on-disc, electro-impedance spectroscopy, and cross hatch tester, respectively. The tribological results reveal that the coated sample of 3 wt-% hBN concentration at 3 mV voltage and 30-minute deposition time shows the lowest friction coefficient (∼0.42) among all the samples, indicating its superior wear resistance and corrosion resistance. Further, the same sample also outperformed the others, demonstrating the high adhesion (adhesion scale of 5 B) of coating with the substrate. Moreover, the surface was characterized using X-ray diffraction, Fourier transforms infrared, goniometer, and scanning electron microscopy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Proceedings of the Institution of Mechanical Engineers, Part J: Journal of Engineering Tribology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.