Transport performance of a HTS current lead prepared by the TFA-MOD processed YBCO tapes

Abstract

A superconducting current lead has been prepared using 12 tapes of the trifluoroacetates – metal organic deposition (TFA-MOD) processed Y 1Ba 2Cu 3O 7- δ (YBCO) coated conductors with critical current ( I c ) of about 100 A at 77 K in self-field. The tapes are 4.5 mm in width, 220 mm in length and about 120 μm in overall thickness. The 1 μm thick superconducting YBCO layer was formed through the TFA-MOD process on Hastelloy TM substrate tapes with two buffer oxide layers of Gd 2Zr 2O 7 (GZO) and CeO 2. The 12 YBCO tapes were arrayed on the both sides (six tapes on each side) of a stainless steel board with 3 mm in thickness for a board type shape. They were similarly soldered to copper caps at the both ends. The transport current of 1000 A was stably applied for 10 min in the liquid nitrogen temperature without any voltage generation in all tapes. Although some voltage in some YBCO tapes generated at the applied currents of about 1100 A, the transport current of 1200 A was successfully applied without quenching. The voltage between both copper caps linearly increased with increasing the transport current, and it was about 300 μV at an applied current of 1000 A. A low joint resistance between the YBCO tapes and the copper caps resulted in small amounts of the Joule heating at the joints when 1000 A was applied. The overall (effective) thermal conductivity of the current leads composed of YBCO tapes and the stainless steel board was much lower than that of Non-superconducting current leads. Therefore, the present current leads with small heat leakage seemed to be practically promising for superconducting magnets.