Abstract
The microstructural evolution of atomised U–7 wt%Mo alloy fuel under irradiation was investigated by transmission electron microscopy on material from the experimental fuel plates used in the FUTURE irradiation. The interaction layer that forms between the U(Mo) particles and the Al matrix is assumed to become amorphous under irradiation and as such cannot retain the fission gas in stable bubbles. As a consequence, gas filled voids are generated between the interaction layer and the matrix, causing the fuel plate to pillow and finally fail. The present analysis confirms the assumption that the U(Mo)–Al interaction layer is completely amorphous after irradiation. The Al matrix and the individual U(Mo) particles, with their cellular substructure, have retained their crystallinity. It was furthermore observed that the fission gas generated in the U(Mo) particles has formed a bubble superlattice, which is coherent with the U(Mo) lattice. Bubbles of roughly 1–2 nm size have formed a 3-dimensional lattice with a lattice spacing of 6–7 nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.