Abstract
Single-crystalline MnOOH and Mn3O4 nanowires have been prepared by hydrothermal treatment of commercial bulky manganese oxide particles. β-MnO2 and α-Mn2O3 nanowires were prepared by calcination of MnOOH nanowires. Transmission electron microscopy analysis demonstrates that MnOOH nanowires grow directly from MnO2 raw particles. The diameter of the nanowires is 20–70 nm, while the length can reach several micrometers. MnOOH nanowires grow preferentially along the [010] direction and Mn3O4 nanowires prefer to grow along the [001] direction; the long dimension of both β-MnO2 and α-Mn2O3 nanowires is along [001]. Electron energy-loss spectroscopy analysis shows that the position of the prepeak of the oxygen K edge shifts to higher energy and the energy separation between the two main peaks of the oxygen K edge decreases with decreasing manganese oxidation state. The manganese-white-line ratios (L3∕L2) were calculated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.