Abstract
The microdomain structures and liquid crystal (LC) orientations of ABA triblock copolymers comprising poly(styrene) (PS) A blocks and a main-chain LC polyester B block were examined via small-angle X-ray scattering and electron microscopy in the form of fibrous samples. The LC polyester blocks were segregated from the PS blocks to form a nematic LC in the lamellar microdomains of the copolymers, with the PS volume fraction (φ) ranging from 13 to 38%. As φ decreased, the nematic director was always positioned along the fiber axis, but the microdomain lamellae changed their direction from parallel to perpendicular with respect to the fiber axis and began to adopt a zigzag configuration. These lamellar orientations were attributed to the main-chain nematic LC segments lying along the microdomain interface but extending perpendicularly to the interface as the occupying interface area was reduced. The lamellar microdomains parallel to the nematic director increased the LC and PS lamellar thicknesses reversibly by 48 and 16%, respectively, at the same time as the isotropization of the nematic LC. Such changes in lamellar thickness suggest that both the PS and LC segments were elongated along the direction of the LC orientation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.