Transient photocurrent responses in amorphous Zn-Sn-O thin films

Abstract

In this study we characterized the transient photocurrent responses in solution-processed amorphous zinc-tin-oxide (a-ZTO) thin films measured under light illumination with a wavelength of 400 nm at different temperatures. By using the temperature-dependent photoconductivities of a-ZTO thin films, we extracted the activation energies (E ac ) of photo-excitation and dark relaxation through an extended stretched exponential analysis (SEA). The SEA was found to describe well the dark relaxation characteristics as well as the photo-excitation processes. The SEA also indicates that the dark relaxation process reveals a dispersive transient photoconductivity with a broader distribution of the E ac while the photo-excitation process shows non-dispersive characteristics. Samples exposed by light at temperatures less than 373 K possess the fast processes of photo-excitation and dark relaxation. This suggests that a fast process, for example, a generation/recombination of charged carriers related to a band-to-band transition and/or shallow/deep oxygen-vacancy (V o ) sub-gap donor states, is dominant in the case of light illumination at low temperatures of less than 373 K. The SEA indicates, however, that a much slower process due mainly to the delay of the onset of ionization/neutralization of the deep V o states by multiple-trapping is dominant for samples under light illumination at a high temperature of 373 K. Based on the experimental results, for the dark relaxation process, we conclude that the process transitions from a fast recombination of electrons through band-to-band transitions and/or shallow/deep V o donor states to a slow neutralization of the ionized V o states occurs due to enhanced carrier multiple-trapping by relatively deep V o trap states when the temperature becomes greater than 363 K. An energy band diagram of a-ZTO thin films was proposed in terms of the temperature and the E ac distribution to explain these observed results.