Abstract
Na-saturated bimessite was synthesized by oxidizing an alkaline MnCl2 solution with gaseous O2. Transmission electron microscopy (TEM) showed no morphological change upon K-saturation of the bimessite, but selected-area diffraction (SAD) revealed structural disorder. Stepwise heating of the K-birnessite to 800°C yielded cryptomelane, as indicated by X-ray powder diffraction (XRD). Various degrees of transformation to the final cryptomelane product were observed by TEM and SAD, but not by XRD. Unaltered bimessite formed chiefly as thin, platy crystals of apparent hexagonal outline. The cryptomelane crystals that formed by heating the K-saturated bimessite were acicular. Bimessite crystals, partially transformed to cryptomelane and displaying non-integral diffraction spots, formed plates having linear striations and rods twinned at 60° to each other. These intermediate products commonly retained some of the original hexagonal appearance of the parent bimessite. Structural disorder was detected in the partially transformed crystals by SAD. TEM revealed 6.8- and 4.8-A spacings of the (110) and (200) planes of cryptomelane, respectively. The basal planes of bimessite layers (001) appeared to correspond topotactically to the (110) plane of cryptomelane during these transformations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.