Abstract
A review of the presently available results for track etching in metallic glasses is given. Latent tracks in amorphous Fe81B13.5Si3.5C2 can be selectively etched to surface pores with a wide cone opening angle. Etched tracks have been observed only if the alloy is in the amorphous and not in the crystalline state. Annealing tests after ion irradiation show that track fading occurs for temperatures above 200°C. An etching threshold is observed at a critical energy loss of 3.4 keV/Å, which is far above the threshold for creating damage (1.3 keV/Å) as observed by resistivity measurements. The etching behaviour near the threshold shows a transition regime from non-homogeneous etching. This observation is related to etched tracks in insulators. The occurrence of the etching threshold is used to determine the influence of the distribution of the radial dose of ions having various velocities. The experimental results are compared with thermal spike calculations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.