Abstract
The influence of calcium phosphate (Ca-P) coating and surface roughness on the trabecular bone response of titanium implants was investigated. Four types of titanium implants, i.e. blasted with titanium powder, sintered with titanium beads, titanium powder blasted and provided with an additional Ca-P coating, and titanium beads with Ca-P coating, were prepared. The Ca-P coating was deposited by ion beam dynamic mixing method. The Ca-P coating was rapid heat-treated with infrared radiation at 700°C. The implants were inserted into the trabecular bone of the left and right femoral condyles of 16 rabbits. After implantation periods of 2, 3, 4 and 12 weeks, the bone-implant interface was evaluated histologically and histomorphometrically. Histological evaluation revealed new bone formation around different implant materials after already 3 weeks of implantation. After 12 weeks, mature trabecular bone surrounded all implants. At 3 and 4 weeks of implantation, no difference existed in bone contact to the various implant materials. On the other hand, after 12 weeks of implantation the highest percentage of bone contact was found around the Ca-P coated beads implants. Supported by the results, we concluded that the combination of surface geometry and Ca-P coating benefits the implant-bone response during the healing phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.