Abstract
The structural evolution and temperature dependence of crystal thickness in high-density polyethylene (HDPE) generated from quasi-isothermal and stress-induced localized melts were studied by employing small-angle X-ray scattering and differential scanning calorimetry techniques. By analyzing the relationship between the reciprocal lamellar thickness and crystallization temperature, two well-defined crystallization lines with similar slopes were obtained, implying an organization of molten chain segments into crystallites passing through a mesomorphic phase. However, two different equilibrium crystallization temperatures were yielded. Furthermore, two recrystallization lines were ascertained for both stretched and isothermal crystallized HDPE samples. These phenomena are mainly caused by the differences between the thermodynamic parameters of polymer chains and crystal stabilities. Specifically, HDPE upon stretching processed much thinner crystalline lamellae, while the sample during isothermal crystallization exhibited better stability due to the high internal mobility of the polymeric chain segments and global flexible surroundings. Moreover, neither melting line coincided with their crystallization lines, which confirmed that these two processes are irreversible.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.