Abstract
In order to examine the threshold condition for the fatigue limit of materials containing a small crack under cyclic torsion, reversed torsional fatigue tests were carried out on 0.47% C steel specimens containing an initial small crack. Initial small semi‐elliptical cracks ranging from 200 to 1000 μm in length were introduced by the preliminary tension–compression fatigue tests using specimens containing holes of 40 μm diameter. The threshold condition for the fatigue limit of the specimens containing artificial small defects under rotating bending and cyclic torsion are also reviewed. Crack growth behaviour from an initial crack was investigated. The torsional fatigue limit for a semi‐elliptical small crack is determined by the threshold condition for non‐propagation of Mode I branched cracks. The torsional fatigue limit of specimens containing an initial small crack can be successfully predicted by the extended application of the √area parameter model in combination with the σθmax criterion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.