Torrefaction at 200 °C of Pubescens Pretreated with AlCl3 Aqueous Solution at Room Temperature.

Abstract

Metal salt soaking–torrefaction conversion technology was investigated. It was found that AlCl3 pretreatment of pubescens favored observably the yield of liquid and small-molecular products in torrefaction via changing the composition and structure of the raw material. The maximum conversion of pretreated samples, washed (PSW) and Yliquid were 15.5 and 10.8 wt % (with 0.26 wt % monosaccharides, 0.26 wt % carboxylic acids, 0.38 wt % furan compounds, and 1.28 wt % phenols), where 20.4 wt % hemicellulose, 22.9 wt % cellulose, and 5.7 wt % lignin were converted, respectively. However, for pretreated samples (PS), the maximum conversion and Yliquid reached 44.2 and 32.1 wt %, respectively, along with 96.0 wt % hemicellulose and 31.8 wt % cellulose converted, yielding 2.39 wt % monosaccharides, 5.14 wt % carboxylic acids, 2.60 wt % furan compounds and 10.52 wt % phenols, indicating obvious catalytic effects of residual AlCl3 on the decomposition of the three major components in torrefaction. Two-dimensional HSQC and electrospray ionization mass spectrometry (ESI-MS) characterizations further confirmed the dominant formation of oligomers derived from holocellulose, lignin, and cross-linkage involving the lignin–carbohydrate complex, indicating that the catalytic thermal cleavage of β-O-4, C-O-C, β-β, 5–5, 4-O-5, Cα–Cβ, and α-O-4 linkages by aluminum species in the samples benefited the yield of liquid as well as monophenols.