Abstract
Molybdates have applications in various fields such as phosphors, optical fibers, scintillators, magnets, sensors and catalysts. Thulium ion is an excellent blue activator and plays an important role in the design of persistent luminescent materials. This paper reports the investigation of the structural and luminescent properties of Barium Thulium Molybdate (Ba1−xTmx)MoO4 microcrystals (with x = 0, 0.01 or 0.03). The scheelite-type crystalline structure was identified from XRD and Raman studies. Under ultraviolet (359 nm) excitation, photoluminescence (PL) spectra present the characteristic emission bands at 453 nm and 545 nm which are due to the D12→F34 and D12→H34,5 transitions, respectively, from Tm3+ ions. Thermoluminescence (TL) measurements were performed with powdered samples previously irradiated with beta radiation. The depth of traps, associated with trap levels located inside the band-gap, was determined from TL data using different methods of glow curve analysis. The kinetic parameters, determined from thermoluminescent glow curves, provide evidence about a possible persistent luminescence emission from the (Ba0.97Tm0.03)MoO4 sample. This is a potential blue-light or ultraviolet long-lasting phosphor, with a trapping level lifetime, at room-temperature (300 K), of about 6 days.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.