Abstract
Titania–hydroxyapatite (HAp) bi-layer coating on Ti metal substrate with improved adhesion strength is fabricated by a simple two step processes: electrodeposition of Ti sol and electrophoretic deposition of HAp powder, followed by heat treatment at 800°C. At optimized process parameters, the bi-layer developed consists of dense, thin and crystalline titania interlayer with porous, thick and crystalline HAp top layer. The heat treatment of bi-layer coating allows elemental intermixing at the interface of TiO2 and HAp, as determined by energy dispersive X-ray spectroscopy (EDX) and Raman spectra analysis. Compared to monolithic HAp coating, the TiO2/HAp bi-layer coating shows significant enhancement in the adhesion strength (48MPa) as well as corrosion resistance without compromising its biocompatibility. The steep increase in adhesion strength is believed to be due to mechanical interlocking and diffusion bonding at the interface. Presence of dense titania interlayer in the bi-layer coating reduces the corrosion current in Ringer's solution to a negligible value (∼100nA).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.