TiO2 with controlled nanoring/nanotube hierarchical structure: Multiabsorption oscillating peaks and photoelectrochemical properties

Abstract

TiO2 with Nanoring/Nanotube (R/T) hierarchical structure can be prepared by tuning the oxidation time and oxidation voltage in the second step anodization. The resulting multiabsorption oscillating peaks in the visible light region present a strong dependence on the tube length which are derived from the interference of light reflected from the top nanorings and the bottom Ti substrate, and the optical path length in TiO2 R/T hierarchical structure can be estimated as about 2μm. The tube length of the as-prepared TiO2 photoelectrode affects greatly its saturation photocurrent density, and the different tube-wall thickness can change the photocurrent-saturation potential. Under simulated AM 1.5 irradiation (100mW/cm2), TiO2 R/T hierarchical structure with tube diameters of 20–40nm and tube length of about 1.5μm shows higher photocurrent density and hydrogen production rate at the bias of 0V (vs. Ag/AgCl). The results from the IPCE plots and I-t curves verify that TiO2 R/T hierarchical structure can exhibit the visible light activity, which is more related to the absorption induced by the defects rather than oscillating peaks. Based on the unique multiple light reflection in TiO2 R/T hierarchical structure, surface treatment will pave a way for the better utilization of oscillating peaks in the visible light region.