Abstract

The major challenges for electrospun membranes used in direct contact membrane distillation (DCMD) process are insufficient pore wetting resistance related with hydrophobicity and pore structure of membrane surface. A novel super-hydrophobization method containing first coating TiO2 nanoparticles on membrane surface by the low temperature hydrothermal process and then the TiO2 coated membrane being fluorosilanized with low surface energy material of 1H, 1H, 2H, 2H-perfluorododecyl trichlorosilane (FTCS) was employed to modify the virgin polyvinylidene fluoride electrospun nanofiber membrane (PVDF ENM). Results showed that this TiO2-FTCS modified membrane possessed high hydrophobicity (157.1°), high mean roughness (4.63μm), considerable wetting resistance (158kPa), well-distributed pore size (0.81μm), reasonable surface porosity (57%) and modest membrane thickness (55μm). These combined properties made the modified PVDF ENM an attractive candidate for DCMD. High flux and stable desalination performances were achieved during short-term DCMD process (73.4LMH permeate flux, 99.99% salt rejection) using 3.5wt% NaCl solution. Long-term DCMD process with actual reverse osmosis brine as feed solution also showed high performance (40.5LMH, 99.98%). These results exceeded those of commercial PVDF membrane and unmodified PVDF ENM significantly, suggesting the potential for PVDF ENM in DCMD applications.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call