Time and Temperature Dependence of the Ultimate Properties of an SBR Rubber at Constant Elongations

Abstract

Abstract A study was made previously of the temperature and strain rate dependence of the stress at break (tensile strength) and the ultimate elongation of an unfilled SBR rubber. In that study, stress-strain curves to the point of rupture were measured with an Instron tensile tester on ring type specimens at 14 temperatures between −67.8° and 93.3° C, and at 11 strain rates between 0.158×10−3 and 0.158 sec−1 at most temperatures. The tensile strength was found to increase with both increasing strain rate and decreasing temperature. At all temperatures above −34.4° C, the ultimate elongation was likewise found to increase with increasing strain rate and decreasing temperature but at lower temperatures the opposite dependence on rate was observed; at −34.4° C, the ultimate elongation passed through a maximum with increasing rate.