Abstract
The three-dimensional vertical-array scaffolds can be constructed by electrostatic flocking with quite high efficiency and low cost for large-area applications. Herein, we have fabricated stretchable and highly conductive fabric base resulting from the strong interaction between acid-functionalized carbon nanotubes (AC-MWNTs) and cationic cotton/spandex fabric. Then the electrostatic flocking was applied for the first time to implant vertical arrays of carbon fibers onto conductive fabrics, accompanied by deposition of nano-MnO2 to construct 3D stretchable fabric-based electrode with multistage array structure (MnO2@C-MC/S1-2). The composite binder-free electrode provided high conductivity and capacitive efficiency as well as the ideal electrochemical reversibility under tension. Furthermore, asymmetric solid-state supercapacitors were assembled using MnO2@C-MC/S1-2 as the positive electrode, C-MC/S1 with higher C1 loaded as the negative electrode, which exhibited maximum energy density of 1.70 mWh/cm2 (at a power density of 21.82 mW/cm2) and power density of 347.34 mW/cm2 (at an energy density of 0.91 mWh/cm2). The facile electrostatic flocking process with simplicity of operation and economic efficiency is both straightforward and cost-effective for fabricating three-dimensional electrodes for wearable energystorageapplications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.