Abstract
A novel thin film nanocomposite reverse osmosis (TFN-RO) membrane was prepared by interfacial polymerization of m-phenylenediamine (MPD) and trimesoyl chloride (TMC) monomers and embedding reduced graphene oxide (rGO)/TiO2 nanocomposite in its polyamide layer. The rGO/TiO2 nanocomposite was added to the MPD solution with aim of improving RO performance, enhancing antifouling property and increasing chlorine resistance. Surface scanning electron microscopy (SEM) images show that all of the membranes have a rough surface with a layer of “ridge-and-valley” structure that is typical morphology of MPD/TMC polyamide membranes. The contact angle analysis showed that hydrophilicity of the membranes was improved by increasing the concentration of rGO/TiO2 due to the presence of various hydrophilic and negatively charged functional groups on the rGO/TiO2 nanocomposite. The superior performance of the rGO/TiO2/RO membrane was observed in the case of 0.02wt% rGO/TiO2 with water flux of 51.3L/m2h and salt rejection of 99.45%. Antifouling ability of the membranes studied by bovine serum albumin (BSA) solution filtration showed that 0.02wt% rGO/TiO2/RO membrane had the best antifouling property. Also, after the chlorination tests, the salt rejection of the bare RO membrane decreased by 30%, while this value was only 3% for 0.02wt% rGO/TiO2/RO membrane which confirmed its great chlorine resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.