Abstract
Abstract The magnetic anisotropy of films of La0.7Sr0.3MnO3 grown on vicinal (1 1 1)-oriented SrTiO3 substrates are investigated. For temperatures above the tetragonal – cubic structural phase transition temperature of the substrate, a step edge induced uniaxial magnetic anisotropy is found at remanence, with a thickness-driven change in easy axis direction, from perpendicular to the step edges to parallel to the step edges with increasing thickness. The anisotropy constant for the investigated (1 1 1)-oriented samples is of the same magnitude as for previously reported (0 0 1)-oriented samples. The data is discussed in the framework of in-plane rotations of the oxygen octahedra resulting in a uniaxial anisotropy. Furthermore, the magnetic anisotropy is sensitive to the structural phase transition at 105 K of the substrate, and the anisotropy constant increases drastically as the temperature is lowered below 105 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.