Abstract
The hydrogen solubility and permeation in Pd77%Ag23% membranes have been determined as a function of temperature and membrane thickness. Unexpectedly, the solubility of hydrogen is found to systematically increase as the membrane thickness decreases from 11.2 to 2.2µm. Topography studies by atomic force microscopy in conjunction with previously reported characterization suggest linkage of the hydrogen solubility to the density of grain boundaries. A higher average grain boundary density for thinner membranes results from the nucleation and growth proceeding during membrane fabrication by sputtering. For the membranes and conditions (no membrane pretreatment; 300–400°C; ΔpH2≤200kPa) applied here, surface phenomena affect the hydrogen transport at thicknesses below ~5µm. Determination of the solubility constants hence allowed the extraction of the bulk diffusivity parameters from the permeability measurements over the thicker membranes (6.7–11.2µm), in good agreement with reported values obtained using other techniques.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call