Abstract
ABSTRACT In the present study, two types of MRE with different concentrations, and circular and rectangular shapes having thicknesses from 6.35mm to a maximum of 25.4mm are prepared. These samples are tested under quasi-static compression and quasi-static double lap shear. It is observed that the measured off-state shear modulus has large variations with increase in the thickness of the sample. The measured shear modulus from the double lap shear test results, as well as the Young's modulus from the compression tests at zero-field, follows a logarithmic trend. With the increase in applied magnetic field, it is observed that the change in modulus shifted from a linear at lower field to a non-linear trend at higher fields. In addition it is observed that the controllability of MRE is more in the compression mode than in the shear mode . Keywords : Thick magnetorheological elastomers, shear , compression, damping, stiffness 1. INTRODUCTION Magnetorheological elastomers (MREs) are made by mixing micro-meter sized magnetizable particles with a non-magnetic elastomeric matrix. MREs are often referr ed to as the solid-state analogues of MR fluids
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.