Abstract
A thick InGaN film was grown on a sapphire substrate by metal organic vapor phase epitaxy using a thin buffer layer of sputter-deposited InGaN. A thick film of highly luminescent In0.2Ga0.8N can be successfully grown at a rate as high as 2 µm/h. The crystal quality of InGaN grown on the sputter-deposited InGaN buffer layer was better than that of InGaN grown directly on the sapphire substrate. The sample showed n-type conduction with a carrier concentration and mobility of 5×1018 cm-3 and 3 cm2/(V·s), respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.