Abstract
AbstractEffects of epoxy resin on various arylamine‐based benzoxazine resins, i.e., aniline (BA‐a), m‐toluidine (BA‐mt), and 3,5‐xylidine (BA‐35x), have been investigated. Processing windows of BA‐35x, BA‐mt, and BA‐a were found to be widened with the amount of the epoxy. Gel points of benzoxazine‐epoxy resin mixtures can be predicted by an Arrhenius equation, e.g., gel time of BA‐35x and epoxy mixture at 70:30 mass ratio can be estimated by tgel = 0.7012 × 10−7 exp (10.563/T). Glass transition temperature (Tg) of BA‐a and BA‐mt alloyed with epoxy exhibited a synergistic behavior with the maximum Tg value at the benzoxazine‐epoxy composition of 80:20 mass ratio. However, in the BA‐35x and epoxy mixture, the decreasing trend in Tg from 241°C to 223°C with an addition of epoxy was observed. Furthermore, flexural strength and strain‐at‐break of those alloys were found to increase with increasing amount of the epoxy while modulus increased with the polybenzoxazine mass fraction. POLYM. ENG. SCI., 2011. © 2011 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.