Abstract
8%Y2O3-stabilized zirconia (8YPSZ) and mullite (3Al2O3·2SiO2) powders, which were made plasma sprayable by using an organic binder (polyvinyl alcohol), have been plasma spray coated on to the piston head, valves and cylinder head of a 3.8kW single-cylinder diesel engine, previously coated with Ni-Cr-Al-Y bond coat. The engine with components coated with 250 μm thick 8YPSZ and 1 mm thick mullite thermal barrier coatings has been evaluated for fuel efficiency and for endurance during 500 h long rigorous tests. Improved fuel efficiency was shown by the engine with coated components and the results are discussed. The coatings and the coated components have also been examined for phases, microstructure and chemical composition by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDAX). Mullite coatings were found to exhibit increased resistance to microcracking compared with 8YPSZ during the 500 h endurance test.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Proceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.