Abstract
The cyclic deformation and fatigue behavior of the γ-TiAl alloy TNB-V5 is evaluated under thermomechanical load for three different microstructures. For this purpose, strain-controlled thermomechanical fatigue (TMF) tests were carried out with different temperature-strain cycles, different temperature ranges from 400 °C to 800 °C (673 K to 1073 K), and with two different strain ranges to set a fatigue-life relation. Cyclic deformation curves, stress-strain hysteresis loops, and fatigue lives of the tests are presented. The microstructures near-gamma (NG) and duplex (DP) show comparable fatigue lives under all test parameters. The microstructure fully-lamellar (FL) offers longer fatigue lives at the same loading conditions. For a general life prediction, the damage parameter of Smith, Watson, and Topper, P SWT vs fatigue life, is well suitable, if the testing and the application temperature ranges, respectively, include temperatures above the ductile-brittle transition (approximately 750 °C). In the completely brittle material behavior regime the quality of the lifetime prediction is unacceptable. The damage parameter P HL by Haibach and Lehrke shows a comparable correlation to the fatigue life as P SWT. The results are discussed with microstructural investigations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.