Abstract
YCa4O(BO3)3 crystal having various concentration of Ce ions were synthesized by solid-state diffusion technique. XRD pattern of the sample confirmed the formation of the sample. Thermoluminescence (TL) and lyoluminescence (LL) of the γ-ray-irradiated sample were recorded. Two distinct peaks around 160 and 277 °C were observed in TL glow curves. TL intensity increased with increasing dopant concentration up to 2 mol%. A single sharp peak was observed in the LL glow curve of the sample. It was found that both TL and LL increased almost linearly with γ-ray doses up to 1.5 kGy. Photoluminescence (PL) of the sample was recorded to find the role of rare earth ion doped in YCa4O(BO3)3. PL emission spectrum showed two peaks lying very close to each other around 390 nm which are characteristics of 5d → 4f transition of Ce3+ ions. When LL of samples was recorded after removing the TL peaks it did not show any emission. This indicates that emission centres responsible for TL are also responsible for LL.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.