Abstract
Thermogravimetric analysis of cupola coke and anthracite samples was carried out using a Setaram derivatograph by means of test charge diluting in powder thermo-inert solvent. Method applicability in comparative evaluation of various carbon materials properties is shown. At heating up to 1500 °C the behavior of coke and anthracite differs slightly; that allows suggesting the possibility of replacing coke by anthracite. Ash residues melt formation and their crystallization during subsequent cooling depends on the amount and composition of ash and can infl uence signifi cantly the course of technologic process.
Highlights
Thermogravimetric analysis of cupola coke and anthracite samples was carried out using a Setaram derivatograph by means of test charge diluting in powder thermo-inert solvent
At heating up to 1500 °C the behavior of coke and anthracite differs slightly; that allows suggesting the possibility of replacing coke by anthracite
Анализ образцов литейного кокса и антрацита показал, что их поведение при нагревании отличается незначительно и, следовательно, антрацит во многих технологических процессах может частично или полностью служить заменителем кокса
Summary
В настоящей работе исследовалось поведение при нагревании с последующим охлаждением литейного кокса марки КЛ-1 и антрацита марки А разреза Красногорский (Кемеровская обл.) методом термогравиметрического анализа на дериватографе фирмы Setaram, позволяющем производить нагрев до 1500 °С. Содержащих небольшое количество золы (5 – %) и летучих веществ (1 – 5 %), тепловыми эффектами их нагрева, а также выделения и возможного окисления летучих веществ можно пренебречь и констатировать, что изменение положения ноль-кривой зависит, в основном, от изменения массы образца, которая в процессе нагрева уменьшается более чем в раз.
Sign-in/Register to view highlights & summary Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Izvestiya Visshikh Uchebnykh Zavedenii. Chernaya Metallurgiya = Izvestiya. Ferrous Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.