Abstract
The high-temperature thermoelectric (TE) properties of group 13 elements (Ga, In, and Tl) triple-filled skutterudites in the nominal compositions of InxGa0.02Tl0.20Co4Sb12 (0 x 0.30) were investigated. All samples contained impurity phases in addition to the skutterudite matrix phase, i.e. some of the filler elements added to CoSb3 precipitated as the metal state and antimonides. With increase the starting amount of In, the actual content of In increases while that of Tl decreases. Owing to phonon scattering by rattling of the group 13 elements, low lattice thermal conductivity was achieved, leading to relatively high TE figure of merit (ZT) for all samples. The maximum ZT value was 0.72 at 773K obtained for the sample in the nominal composition of In0.30Ga0.02Tl0.20Co4Sb12. [doi:10.2320/matertrans.E-M2014826]
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.