Abstract
Boron carbide (B4C) composites containing 0–10 wt.% graphene nanoplatelets (GNPs) were consolidated using hot pressing at 1950 °C for 60 min under 30 MPa in an argon atmosphere. Their electrical discharge machining (EDM) characteristics were evaluated for the first time. Additionally, the effects of GNPs on the microstructure, electrical conductivity, material removal rate (MRR), and surface roughness (Ra) of B4C composites were investigated. The results show that the B4C composite containing 10 wt.% GNPs exhibited the highest electrical conductivity of 4997 S·m−1 because of the formation of GNPs conductive networks. Under a fine machining condition, the MRR of the B4C composite was enhanced by 43.5 % (from 6.55 to 9.40 mm3 min−1) compared with that of monolithic B4C. Furthermore, the Ra decreased to 1.12 μm, which was significantly lower than that of pure B4C (2.44 μm). Scanning electron microscope and energy disperse spectroscopy analysis of the EDM surfaces were used to determine that the main material removal mechanisms for B4C composites with less than 2 wt.% GNPs were spalling and melting. As the GNPs content increased, B4C grain fallout, melting, and evaporation became more dominant. The other mechanisms, including thermal shock and oxidation, are also discussed in detail.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.