Abstract
Since many thermoelectrics are brittle in nature with low mechanical strength, improving their mechanical properties is important to fabricate devices such as thermoelectric power generators and coolers. In this work, multiwalled carbon nanotubes (CNTs) were incorporated into polycrystalline Bi0.4Sb1.6Te3 through powder processing, which increased the flexural strength from 32 MPa to 90 MPa. Electrical and thermal conductivities were both reduced in the CNT containing materials, leading to unchanged figure of merit. Dynamic Young's and shear moduli of the composites were lower than the base material, while the Poisson's ratio was not affected by CNT doping.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.