Abstract
The non-metallic inclusions in steel mainly come from the deoxidization process of molten steel. Based on the different deoxidization processes of GCr15 bearing steel produced by a domestic steel plant, the single deoxidization curves of Al, Si, and Mn and the compound deoxidization curves of Al-Si and Si-Mn under pure molten iron and GCr15 bearing steel production conditions were calculated with the FactSage 8.1 thermodynamic software. The results show that the deoxidization curves under the two conditions are quite different. At the same time, the Al-Ti deoxidation equilibrium curve under the condition of GCr15 bearing steel was calculated. It was found that when [Ti] < 0.0015% in the steel, the equilibrium deoxidation product was Al2O3, and no titanium oxide was generated. Finally, a thermodynamic calculation and analysis of the effect of rare-earth Ce content on the modification of inclusions in GCr15 bearing steel were carried out. The results showed that when T = 1873 K, the rare-earth Ce treatment of aluminum deoxidized the GCr15 bearing steel; when [Al] = 0.015%, Al2O3 inclusions increased with the increase in [Ce] content, and the evolution path was Al11O18Ce→CeAlO3→Ce2O3. When [Si] = 0.28%, [O] > 50 ppm, and CeCrO3 and [O] 0.012% appeared. CeS inclusions appeared in the steel, and the final equilibrium product was CeS + Ce2O3. When [Ce] < 0.012%, CeS was not produced in the steel, and only Ce2O3 existed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.