We present theoretical and experimental results regarding the thermodynamic stability of the high-k dielectrics ZrO2 and HfO2 in contact with Si and SiO2. The HfO2/Si interface is found to be stable with respect to formation of silicides whereas the ZrO2/Si interface is not. The metal–oxide/SiO2 interface is marginally unstable with respect to formation of silicates. Cross-sectional transmission electron micrographs expose formation of nodules, identified as silicides, across the polycrystalline silicon/ZrO2/Si interfaces but not for the interfaces with HfO2. For both ZrO2 and HfO2, the x-ray photoemission spectra illustrate formation of silicate-like compounds in the MO2/SiO2 interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.