Coarse grained WC–9Co cemented carbides with 0–1.0% TaC (mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDS), X-ray diffractometry (XRD) and mechanical properties tests. The results show that the maximum values of hardness and strength are HV 1124 and 2466 MPa respectively when 0.4% TaC is added. When the content of TaC is more than 0.6%, the grain size of WC is no longer affected by the amount of TaC, and (W,Ta)C occurs as well. Moreover, the strength and fracture toughness increase and the (Ta+W) content decreases with the increase of TaC content. The dependence of (Ta+W) content on the mechanical properties indicates that (Ta+W) content in Co should be decreased as low as possible to improve the mechanical properties of coarse grained WC–TaC–9Co cemented carbides with the microstructure of WC+γ two phase regions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.