Abstract
This study focuses on thermo-mechanical fatigue (TMF) behaviors of nickel-based 23Cr-45Ni-7W alloy for pipes and tubes in high-efficiency power boilers. TMF tests (maximum temperature = 700 °C; minimum temperature = 100 °C) were conducted under in-phase (IP) and out-of-phase (OP) conditions. The lives under the IP condition is 0.30–0.44 times of that under the OP condition when same total strain range, Δεt, is applied. The TMF properties obtained via the tests are compared with the results of isothermal fatigue (ITF) tests conducted at 700 °C and bithermal fatigue (BTF) tests with maximum and minimum temperatures of 700 °C and 100 °C, respectively. The fracture morphology for each type of TMF, ITF, and BTF is similar under the test conditions of this study. Intergranular cracking is predominant under application of cyclic tensile creep strain during the fatigue tests, and transgranular cracking is predominant under application of cyclic compressive creep strain during the fatigue tests. The inelastic strain range–fatigue life (Δεin–Nf) relation in the TMF test and the inelastic strain range components–life (Δεij–Nij) relation determined using the strain range partitioning method show a good agreement within a factor of 1.5 scatter band. These results indicate the possibility of predicting the TMF life of the 23Cr-45Ni-7W alloy using the results of the ITF test by considering the amount and direction (tension or compression) of creep strain applied to the alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.