Abstract
Thermal expansion of (Sr1−x , K2x )Zr4(PO4)6 (SrKZP) (with x = 0–1) ceramic was investigated using both a dilatometer and a high-temperature X-ray diffractometer. The coefficients of thermal expansion (CTEs) of the SrKZP ceramic measured by the dilatometer demonstrate a similar trend as those from high-temperature X-ray diffraction. Both measurements show an ultra-low CTE at x = 0.5; nevertheless, this composition shows significant lattice thermal-expansion anisotropy (TEA), while the minimum TEA appears with composition x = 0.2. Although it possessed a sufficient degree of TEA, the x = 0.5 composition showed no visible microcracks or negligible microcracks over a grain size as large as 15 μm. A transition of space group from R{\bar 3} to R{\bar 3}c with composition between x = 0.3 and x = 0.5 has been observed. The crystal structure of the SrKZP ceramic with possible occupations of strontium and/or potassium within the lattice in relation to their influence on the CTEs is proposed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.