Abstract

Thermally rearranged (TR) polymers exhibited a good balance of high permeability and high selectivity. For this purpose HAB-6FDA polyimide was synthesized from 3,3 dihydroxy-4,4-diamino-biphenyl (HAB) and 2,2-bis-(3,4-dicarboxyphenyl) hexafluoro propane dianhydride (6FDA) by chemical imidization. Initially, the sample was modified from pure polymer to silica nanofiller doped polymer membrane. Further the modification was done by thermal rearrangement reaction at 350 °C temperature. This modification causes a mass loss in polymer structure and therefore enhances the fractional free volume (FFV). The gases used for the permeation test were H2, CO2, N2 and CH4. Selectivity was calculated for H2/CO2, H2/N2 and H2/CH4 gas pairs and plotted in the Robeson's 2008 upper bound and compared with reported data. The transport properties of these gases have been compared with the unmodified membrane. Permeability of all the gases has increased to that of unmodified polymer membrane. Thermally rearranged polymer nanocomposite exhibits higher gas permeability than that of silica doped and pure polymer. Also the selectivity for H2/CO2 and H2/N2 gas pairs exceeds towards Robeson's upper bound limit. It crosses this limit dramatically for H2/CH4 gas pair. Polymer nanocomposite can be utilized to obtain high purity hydrogen gas for refinery and petrochemical applications.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call