Abstract
Polycrystalline Ca3-xMgxCo4O9（x=0-0.3）ceramics were prepared by the sol–gel method combined with the ordinary pressing sintering and the thermal conductivities were measured from room temperature to 673 K. The influence of Mg2+ substitution for Ca2+ on the thermal conductivities of Ca3Co4O9 ceramics was investigated systematically. The influence of Mg doping on the thermal conductivities is mainly embodied in the lattice thermal conductivities, which shows a significant decrease with the increase of the dopant content for the samples with x ≤ 0.2, while the carrier thermal conductivity had no obvious change with Mg doping increasing. These results indicated that the thermal conductivities of the material could be reduced remarkably with the substitution of Mg from 1.427 W/m·K to 0.731 W/m·K at 573 K with x = 0.2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.