Thermal transfer and interaction mechanisms of localized excitons in families of InAs quantum dashes grown on InP(001) vicinal substrate emitting near 1.55 μm wavelength

Abstract

With the help of photoluminescence Spectroscopy (PLS), we have investigated the optoelectronic properties of two different families of InAs quantum dashes (QDashes) grown on misoriented InP(001) substrate with 2[Formula: see text]off miscut angle toward the [110] direction (2[Formula: see text]F type). The lowest full width at half maximum (FWHM) of the PL spectrum measured at 12 K indicates the good self organization of InAs QDashes. The weak ratio of the integrated PL measured in 12–300 K temperature range denotes the good spatial confinement of the photogenerated carriers in InAs QDashes. The fast redshift of the PL peaks energy and the anomalous decrease of the FWHM with the increase of the temperature are attributed to an efficient thermal relaxation process of photogenerated carriers in the vicinal sample. This result is highlighted with the help of theoretical modeling of the PL peak energy as a function of the temperature, using three models (Varshni, “Vina, Logothetidis and Cardona” and Pässler). From experimental and theoretical results, we have evidenced the contribution of longitudinal acoustic-phonons (LA-phonons) in the PL of InAs/InP QDashes, via the deformation potential, especially in high temperatures range. We have attributed this behavior to the strained InAs/InP QDashes and/or to the topography of the vicinal InP(001) substrate which favors the presence of stepped phonons polarized along the steps. These vibrational modes can further interact with the excitons at high temperatures. The measured thermal activation energies of each family of InAs QDashes demonstrate that the InAs wetting layer act as a barrier for the thermoionic emission of photogenerated carriers. This result confirms the good spatial confinement of excitons in this sample.