https://doi.org/10.7567/1347-4065/ab25ba
Copy DOIJournal: Japanese Journal of Applied Physics | Publication Date: Jun 24, 2019 |
Citations: 10 | License type: iop-standard |
We investigate the Ni–Si film silicidation process on 4H-SiC and Si substrates and compare the thermal stability of the films grown on each substrate. The Ni–Si films were subjected to rapid thermal annealing (RTA) in the temperature range 575 °C–975 °C for 90 s, and their thermal stability was characterized by in-situ temperature-dependent sheet resistance measurements at temperatures of 25 °C–550 °C. The sheet resistance of a 40 nm thick Ni film was observed to increase sharply above 330 °C in the Ni/Si (100) interface, but slightly decrease at approximately 480 °C in the Ni/4H-SiC interface. The thermal stability of the films was found to be significantly dependent on the RTA temperature. Thermally stable Ni–Si silicide films with excellent Ohmic properties (no hysteresis behavior) can be obtained on 4H-SiC substrates at RTA temperatures of 925 °C–975 °C and can used for application in MOSFET devices.
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.