Abstract
Thermal stability, oxygen non-stoichiometry and electrical conductivity of LaNi 0.6Fe 0.4O 3 − δ were investigated in the temperature region of 20–1000 °C in Ar/O 2 gas flows at oxygen partial pressures between 0.5 and 21,000 Pa. Diffusion mobility was measured in Ar/O 2 gas flow at pO 2 = 18 Pa. Crystal structure of this compound was found to be stable at the mentioned experimental conditions. LaNi 0.6Fe 0.4O 3 − δ is a p-type semiconductor with metallic type conductivity above 150 °C at the investigated pO 2 range. Two different (fast and slow) oxygen exchange areas on the temperature-pO 2 diagram were established, which are due to two different oxygen anion positions in the double B-site mixed perovskite structure. Oxygen non-stoichiometry in the fast oxygen exchange region reaches about 0.005 of oxygen atomic index. Chemical diffusion and oxygen surface exchange coefficients do not vary at 600–800 °C, but show visible increase above 800–850 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.