Abstract
Lanthanum zirconate (La2Zr2O7, LZ) is a newly proposed material for thermal barrier coatings (TBCs). The thermal stability of LZ coating was studied in this work by long‐term annealing and thermal cycling. After long‐term annealing at 1400°C or thermal cycling, both LZ powder and plasma‐sprayed coating still kept the pyrochlore structure, and a preferred crystal growth direction in the coating was observed by X‐ray diffraction. A considerable amount of La2O3 in the powder was evaporated in the plasma flame, resulting in a nonstoichiometric coating. Additionally, compared with the standard TBC material yttria‐stabilized zirconia (YSZ), LZ coating has a lower thermal expansion coefficient, which leads to higher stress levels in a TBC system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.