Abstract
Here, thermal stabilities for Ohmic contact properties of Pt, Au, and Pd on the same hydrogen-terminated diamond (H-diamond) epitaxial layer are investigated. A long-term annealing process is performed with an annealing temperature and time of 400 °C and 8 h, respectively. Before annealing, good Ohmic contact properties are observed for only two contacts of the Pt/H-diamond and Pd/H-diamond with specific contact resistivity (ρC) values of 2.7 × 10−3 Ω cm2 and 2.6 × 10−4 Ω cm2, respectively. After long-term annealing, all three contacts on the H-diamond show good Ohmic contact properties. The ρC values for the Pt/H-diamond and Au/H-diamond are 3.1 × 10−2 Ω cm2 and 4.2 × 10−4 Ω cm2, respectively. They are higher than that of the Pd/H-diamond (1.1 × 10−4 Ω cm2). Therefore, low ρC and good thermal stability for the Pd/H-diamond are achieved. This is meaningful for pushing forward the development of H-diamond-based electronic devices for high-temperature applications.
Highlights
For H-diamond-based metal–oxide–semiconductor field-effect transistors (MOSFETs), another important consideration is high-temperature applications
Good Ohmic contact properties are observed for only two contacts of the Pt/H-diamond and Pd/H-diamond with specific contact resistivity values of 2.7 × 10−3 Ω cm2 and 2.6 × 10−4 Ω cm2, respectively
It was reported that H-diamond-based MOSFETs could work well at temperatures as high as 400 ○C.13
Summary
For H-diamond-based MOSFETs, another important consideration is high-temperature applications. Thermal stabilities for Ohmic contact properties of Pt, Au, and Pd on the same hydrogen-terminated diamond (H-diamond) epitaxial layer are investigated. Good Ohmic contact properties are observed for only two contacts of the Pt/H-diamond and Pd/H-diamond with specific contact resistivity (ρC) values of 2.7 × 10−3 Ω cm2 and 2.6 × 10−4 Ω cm2, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.