Abstract
The thermal stability and structural characteristics for gate stack structure of HfO2 dielectrics deposited by atomic-layer deposition (ALD) were investigated. The structural characteristics and chemical state of the HfO2 films in relation to the film thickness and postannealing temperature were examined by x-ray diffraction and x-ray photoelectron spectroscopy. An interfacial layer of hafnium silicate with an amorphous structure was grown on the oxidized Si substrate at an initial growth stage. The structural characteristics of the HfO2 films are closely affected by the interfacial layer and are depended on the thickness of the films. The 45 Å thick HfO2 film with an amorphous structure was changed into a polycrystalline structure after rapid temperature annealing of 750 °C for 5 min, while thicker films were grown into a polycrystalline structure of monoclinic or tetragonal crystal structure. The silicate layer grown at the interfacial region is not stable even at 700 °C under ultrahigh vacuum condition and changes into the silicide layers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.