Abstract
The coefficient of thermal expansion of core and veneer porcelains for all ceramic crowns must be compatible to prevent formation of stresses during the firing cycles. The purpose of this study was to use a thermal shock test to evaluate the crazing resistance of six all-ceramic crown systems. The systems tested were: Vita In-Ceram, Vita Hi-Ceram, Dicor veneered with Vitadur N, magnesia core veneered with Ceramco II, magnesia core veneered with Silhouette, and magnesia core veneered with Vita VMK 68. A maxillary central incisor was prepared with 1.0 mm axial and 1.5 mm incisal reduction. Refractory dies were prepared and crowns were fabricated using the manufacturers' recommendations. Six specimens of each system were placed inside a beaker in a furnace at 90 degrees C. After 15 min heat soak, ice water was poured into the beaker through a funnel. The samples were dried in air, reheated, and inspected for crazing using light microscopy. If crazing was observed, this would constitute a failure at a temperature difference (delta T) of 90 degrees C. If no failure occurred, the test was repeated at increasing temperature increments of 10 degrees C until failure. The crazing resistance of each system, expressed as the mean delta T, was: > 200 (Hi-Ceram), 163 +/- 14 (In-Ceram), 152 +/- 19 (Dicor/Vitadur N), 143 +/- 5 (magnesia core/Vita VMK 68), 122 +/- 21 (magnesia core/Silhouette), and 118 +/- 10 (magnesia core/Ceramco II) degrees C. All systems tested resisted crazing due to quenching in ice cold water from 100 degrees C. Systems with lower coefficients of expansion showed significantly greater resistance to thermal shock using ANOVA.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.