Abstract

The impact of the penetration of small quantities of calcium-magnesium-alumino- silicates (CMAS) glassy melt in the porous plasma-sprayed (PS) thermal barrier coatings (TBCs) is often neglected even though it might play a non-negligible role on the sintering and hence on the thermal insulation potential of TBCs. In this study, the sintering potential of small CMAS deposits (from 0.25–3 mg.cm−2) on freestanding yttria-stabilized zirconia (YSZ) PS TBCs annealed at 1250 °C for 1 h was investigated. The results showed a gradual in-depth sintering with increasing CMAS deposits. This sintering was concomitant with local transformations of the tetragonal YSZ and resulted in an increase in the thermal diffusivity of the coatings that reached a maximum of ∼110 % for the fully penetrated coating.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.